| PMMA-VH001/三菱丽阳 | |||||
| ①原料描述部分 | |||||
| 规格级别 | 注塑 | 外观颜色 | |||
| ②原料技术数据 | |||||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hr | ASTM D-570 | MF｜V | % |
| 0.3｜0.3 | |||||
| 熔体流动速率 | 230℃,3.8kg | ASTM D-1238 | MF｜V | g/10min | |
| 2.0｜2.5 | |||||
| 物理性能 | 全光线透射系数 | 3.2mm | ASTM D-1003 | MF｜V | % |
| 93｜93 | |||||
| 比重 | ATSM D-792 | MF｜V | |||
| 1.19｜1.19 | |||||
| 折射率 | ASTM D-542 | MF｜V | |||
| 1.49｜1.49 | |||||
| 机械性能 | 洛氏硬度 | ASTM D-785 | MF｜V | M scale | |
| 100｜95 | |||||
| 延伸率 | ASTM D-638 | MF｜V | % | ||
| 5｜5 | |||||
| 悬臂梁式冲击强度 | 1/4″付 | ASTM D-255 | MF｜V | Kg·cm/cm | |
| 1.7｜1.6 | |||||
| 抗拉强度 | ASTM D-638 | MF｜V | Kg/cm2 | ||
| 740｜730 | |||||
| 抗压强度 | ASTM D-695 | MF｜V | Kg/cm2 | ||
| 1100｜1100 | |||||
| 弯曲弹性模量 | 1/4″棒 | ASTM D-790 | MF｜V | Kg/cm2 | |
| 3.2×104｜3.1×104 | |||||
| 抗弯强度 | 1/4″棒 | ASTM D-790 | MF｜V | Kg/cm2 | |
| 1100｜1100 | |||||
| 电气性能 | 耐电弧性 | JIS K-6911 | MF｜V | ||
| 没有痕迹｜没有痕迹 | |||||
| 绝缘击穿强度 | MF｜V | ||||
| 20｜20 | |||||
| 介电常数 | 60Hz | MF｜V | |||
| 3.7｜3.7 | |||||
| 表面电阻系数 | JIS K-6911 | MF｜V | |||
| >1016｜>1016 | |||||
| 介质损耗角正切 | 60Hz | MF｜V | |||
| 0.05｜0.05 | |||||
| 体积电阻系数 | JIS K-6911 | MF｜V | |||
| >1015｜>1015 | |||||
| 加工性能 | 成形收缩率 | ASTM D-955 | MF｜V | % | |
| 0.2-0.6｜0.2-0.6 | |||||
| 热性能 | 维卡软化温度 | 1kg | ASTM D-1525 | MF｜V | ℃ |
| 116｜107 | |||||
| 热传导系数 | ASTM C-177 | MF｜V | Cal/s/cm/℃ | ||
| 5×10-4｜5×10-4 | |||||
| 比热 | MF｜V | Cal/g/℃ | |||
| 0.35｜0.35 | |||||
| 线膨胀系数 | ASTM D-696 | MF｜V | Cm/cm/℃ | ||
| 6×10-5｜6×10-5 | |||||
| 载荷挠曲温度 | 18.56kg/cm2 | ASTM D-648 | MF｜V | ℃ | |
| 102｜92 | |||||