| PA6T A350 三井石油化学有限公司（日本） 技术指数 |
| 暂无此原料描述部分[规格级别、外观颜色、用途说明都为空]！ |
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 23℃ | ASTM D-570 | 0.2 | % |
| 物理性能 | 模具收缩率 | 2mmt | ASTM D-955 | 0.2 | % |
| 比重 | --- | ASTM D-792 | 1.63 | --- | |
| 机械性能 | 拉伸强度 | dry(moist) | ASTM D-638 | 300(270) | MPa |
| 拉伸伸长率 | dry(moist) | ASTM D-638 | 3(3) | % | |
| 弯曲强度 | dry(moist) | ASTM D-790 | 430(390) | MPa | |
| 弯曲模量 | dry(moist) | ASTM D-790 | 17000(15000) | MPa | |
| IZOD缺口冲击强度 | dry(moist) | ASTM D-256 | 150(160) | J/M | |
| 洛氏硬度 | --- | ASTM D-785 | 110 | M scale | |
| 电气性能 | 体积电阻率 | dry | ASTM D-257 | 1016 | Ω.cm |
| 介电常数 | 1016Hz,dry | ASTM D-150 | 4.5 | --- | |
| 损耗因数 | 1016Hz,dry | ASTM D-150 | 0.018 | --- | |
| Dielectric breakdown voltage | dry | ASTM D-149 | 29 | KV/mm | |
| 热 性 能 | 熔点 | --- | --- | 320 | ℃ |
| 玻璃转变温度 | --- | --- | 125 | ℃ | |
| 负荷挠曲温度 | --- | ASTM D-648 | 310 | ℃ | |
| 线性热膨胀系数 | --- | ASTM D-696 | 1.8 | ×10-5/℃ | |
| 阻燃性 | --- | UL 94 | HB | --- | |
| 其它性能 | Glass fiber content | --- | --- | 50 | % |