| PA12-3035U-日本宇部 | |||||
| ①原料描述部分 | |||||
| 规格级别： | --- | 外观颜色： | --- | ||
| 备注说明： | 特性：高粘度 | ||||
| ②原料技术数据 | |||||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | --- | ASTM D-570 | 0.25 | % |
| 吸水率 | --- | ASTM D-570 | 1.5 | % | |
| 成型收缩率 | --- | UBEmethod | 1 | % | |
| 成型收缩率 | --- | UBEmethod | 1.6 | % | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.02 | --- |
| 机械性能 | 屈服下的伸张强度 | -30° | ASTM D-638 | 770 | kgf/cm2 |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 430 | kgf/cm2 | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 380 | kgf/cm2 | |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 190 | kgf/cm2 | |
| 断裂下的伸张强度 | 23° | ASTM D-638 | >550 | kgf/cm2 | |
| 断裂下的伸张强度 | 23° | ASTM D-638 | >500 | kgf/cm2 | |
| 屈服下的延伸率 | 23° | ASTM D-638 | 12 | % | |
| 屈服下的延伸率 | 23° | ASTM D-638 | 19 | % | |
| 断裂下的延伸率 | 23° | ASTM D-638 | >250 | % | |
| 弯曲强度 | -30° | ASTM D-790 | 880 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 560 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 380 | kgf/cm2 | |
| 弯曲强度 | 80° | ASTM D-790 | 170 | kgf/cm2 | |
| 弯曲弹性率 | -30° | ASTM D-790 | 17000 | kgf/cm2 | |
| 弯曲弹性率 | 23° | ASTM D-790 | 14500 | kgf/cm2 | |
| 弯曲弹性率 | 23° | ASTM D-790 | 10000 | kgf/cm2 | |
| 弯曲弹性率 | 80° | ASTM D-790 | 3400 | kgf/cm2 | |
| 抗冲击强度 | -30° | ASTM D-256 | 8 | kgf.cm/cm | |
| 抗冲击强度 | 23° | ASTM D-256 | 13 | kgf.cm/cm | |
| 抗冲击强度 | 23° | ASTM D-256 | 22 | kgf.cm/cm | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 110 | --- | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 105 | --- | |
| 挤剪强度 | 23° | ASTM D-732 | 350 | kgf/cm2 | |
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 130 | kgf/cm2 | |
| TABER磨耗率 | --- | ASTM D-1044 | 5 | mg | |
| 电气性能 | 体积电阻率 | --- | ASTM D-257 | 1015 | Ω.cm |
| 体积电阻率 | --- | ASTM D-257 | 1014 | Ω.cm | |
| 绝缘耐力 | --- | ASTM D-149 | 30 | KV/mm | |
| 介电常数 | 60HZ | ASTM D-150 | 3.4 | --- | |
| IEC电路 | --- | UL746 | 600+ | V | |
| 介电损耗 | 106HZ | ASTM D-150 | 0.02 | --- | |
| 抗电弧强度 | --- | ASTM D-495 | 180 | S | |
| 介电常数 | 103HZ | ASTM D-150 | 3.3 | --- | |
| 介电常数 | 106HZ | ASTM D-150 | 2.9 | --- | |
| 介电损耗 | 60HZ | ASTM D-150 | 0.03 | --- | |
| 介电损耗 | 103HZ | ASTM D-150 | 0.03 | --- | |
| 热 性 能 | 熔点 | --- | ASTM DSC | 176-180 | °C |
| 线性热膨胀系数 | --- | ASTM D-696 | 10 | X的10-5cm/cm/°C | |
| 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 145 | °C | |