| PA12-3035JL1-日本宇部 | |||||
| ①原料描述部分 | |||||
| 规格级别： | --- | 外观颜色： | --- | ||
| 备注说明： | 特性：韧性,黑色 | ||||
| ②原料技术数据 | |||||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | --- | ASTM D-570 | 0.2 | % |
| 吸水率 | --- | ASTM D-570 | 1.4 | % | |
| 成型收缩率 | UBEmetho | --- | 0.7 | % | |
| 成型收缩率 | --- | UBEmethod | 1.8 | % | |
| 物理性能 | 比重 | --- | ASTM D-792 | 1.03 | --- |
| 机械性能 | 抗冲击强度 | 23° | ASTM D-256 | 30 | kgf.cm/cm |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 80 | --- | |
| 剪切强度 | 23° | ASTM D-732 | 250 | kgf/cm2 | |
| TABER磨耗率 | --- | ASTM D-1044 | 7 | mg | |
| 屈服下的伸张强度 | -30° | ASTM D-638 | 670 | kgf/cm2 | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 270 | kgf/cm2 | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 250 | kgf/cm2 | |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 120 | kgf/cm2 | |
| 断裂下的伸张强度 | 23° | ASTM D-638 | >440 | kgf/cm2 | |
| 断裂下的伸张强度 | 23° | ASTM D-638 | >410 | kgf/cm2 | |
| 断裂下的延伸率 | 23° | ASTM D-638 | >300 | % | |
| 弯曲强度 | -30° | ASTM D-790 | 900 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 200 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 180 | kgf/cm2 | |
| 弯曲强度 | 80° | ASTM D-790 | 110 | kgf/cm2 | |
| 弯曲弹性率 | -30° | ASTM D-790 | 22500 | kgf/cm2 | |
| 弯曲弹性率 | 23° | ASTM D-790 | 4200 | kgf/cm2 | |
| 弯曲弹性率 | 23° | ASTM D-790 | 4000 | kgf/cm2 | |
| 弯曲弹性率 | 80° | ASTM D-790 | 2200 | kgf/cm2 | |
| 抗冲击强度 | -30° | ASTM D-256 | 5 | kgf.cm/cm | |
| 电气性能 | 体积电阻率 | --- | ASTM D-257 | 1012 | Ω.cm |
| 介电损耗 | 106HZ | ASTM D-150 | 0.11 | --- | |
| 介电损耗 | 60HZ | ASTM D-150 | 0.14 | --- | |
| 介电损耗 | 103HZ | ASTM D-150 | 0.21 | --- | |
| 绝缘耐力 | --- | ASTM D-149 | 28 | KV/mm | |
| 介电常数 | 60HZ | ASTM D-150 | 11.8 | --- | |
| 介电常数 | 103HZ | ASTM D-150 | 8.3 | --- | |
| 介电常数 | 106HZ | ASTM D-150 | 3.5 | --- | |
| 热 性 能 | 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 135 | °C |
| 熔点 | DSC | --- | 166-170 | °C | |
| 线性热膨胀系数 | --- | ASTM D-696 | 12 | X的10-5cm/cm/°C | |
| 燃烧率 | --- | UL-94 | HB | --- | |