类别： LCP E5008
功能：玻纤强化
生产厂商：日本住友化学
详细信息：
| 塑料名称(Polymer) | LCP | ||
| 厂商名称(Company) | Sumitomo Chem Co 住友化学 | ||
| 商品名称(Trade Name) | SUMIKASUPER | ||
| 规格(Grade) | E5008 | ||
| 特征(Characteristic) | 玻纤强化 | ||
| 加工方法(Process Method) | |||
| 物性名称 | 单位 | 测试方法 | |
| 填充剂含量 Filler Content |
％ | ASTM D2584 | 40.00 |
| 比重 Specific Gravity |
g/cm³ | ASTM D792 | 1.69 |
| 融点 Melting Point |
℃ | ||
| 流动指数 MFR,(MI) |
g/10 min | ||
| 吸湿率@24h/23℃ Water Absorption |
％ | ASTM D570 | 0.02 |
| 成形收缩率 MD(Mold Shrinkage) |
％ | ASTM D955 | 0.06 |
| 成形收缩率 TD(Mold Shrinkage) |
％ | ASTM D955 | 1.25 |
| 伸张断裂强度 Tensile Strength at Break |
MPa | ASTM D638 | 111.00 |
| 伸张降伏强度 Tensile Strength at Yield |
MPa | ||
| 断裂伸张率 Tensile Elongation at Break |
％ | ASTM D638 | 4.80 |
| 伸张弹性系数 Tensile Modulus |
MPa | ||
| 弯曲强度 Flexural Strength |
MPa | ASTM D790 | 127.00 |
| 弯曲弹性系数 Flexural Modulus |
MPa | ASTM D790 | 12000.00 |
| 艾氏耐冲击强度(缺口式) Izod Impact Strength (notched) |
J/m | ASTM D256 | 88.00 |
| 洛式硬度或秀尔硬度 Rockwell/Shore Hardenes |
|||
| 热变形温度 0.46 MPa Heat Distortion Temp |
℃ | ||
| 热变形温度 1.82 MPa Heat Distortion Temp |
℃ | ASTM D648 | 335.00 |
| 线膨胀系数10¯5 Coefficient of Linear Thermat Expansion |
mm/mm/℃ | ASTM D696 | 6.40 |
| 介电强度 Dielectric Strength |
kV/mm | ||
| 介电常数 Dielectric Constant |
MHz | ASTM D150 | 4.20 |
| 耐电弧性 Arc Resistance |
Sec | ASTM D495 | 128.00 |