| ABS PA-756H 高流动级 | ||||
| 特性：超高流动性 | ||||
| 应用：磁碟片外壳 | ||||
| 物性指标 | ||||
| 特性 | 测试方法 | 测试条件 | 单位 | 数值 |
| 引张强度 | ASTM D638 | 1/8″，6mm/min | Kg/cm2(lb/in2) | 400(5670) |
| Tensile Strength | ||||
| 延伸率 | ASTM D638 | 1/8″，6mm/min | % | 10 |
| Tensile Elongation | ||||
| 弯曲强度 | ASTM D790 | 1/4″,2.8mm/min | Kg/cm2(lb/in2) | 640（9070） |
| Flexural Strength | ||||
| 弯曲弹性率 | ASTM D790 | 1/4″,2.8mm/min | Kg/cm2(lb/in2) | 2300(320000) |
| Flexural Modulus | ||||
| Izod冲击强度 | ASTM D256 | 1/4″,23℃ | Kg.cm/cm | 8（1.5) |
| Izod Impact Strength | (Notched) | 1/8″, 23℃ | (ft.lb/in) | 10（2.9) |
| 流动系数 | ASTM D1238 | 200℃,5Kg | g/10min | 8.5 |
| Melt Flow Index | ||||
| 硬度 | ASTM D785 | 1/2″ | R Scale | 115 |
| Hardness | ||||
| 比重 | ASTM D792 | 23℃ | - | 1.04 |
| Specific Gravity | ||||
| 软化点 | ASTM D1525 | 1/8″,50℃/hr | ℃( ? ) | 105(221) |
| Vicat Softening Temp | ||||
| 热变形温度 | ASTM D648 | 1/4″, 120℃/hr | ℃( ? ) | 99(210) |
| HDT | 89(192) | |||
| 燃烧率 | UL94 | - | - | 1/6″HB |
| Flammability | ||||
| 以上数据仅代表一般通用数据，不代表每一产品的规格值。 | ||||
| 加工条件 | ||||
| 于80℃下烘料约2-3小时； | ||||
| 射出套筒温度介于180-230℃； | ||||
| 模温为30-70℃； | ||||
| 在射出周期中勿将热融胶长期停留在加热管中。 | ||||
| 备注 | ||||
| 符合UL、FDA、日本厚生省及总铅、总镉重金属等检验之规范 | ||||